Material Handling
Aegis® H135ZP homopolymer is supplied in sealed containers and drying prior to processing is not required. However, high moisture is the primary cause of processing problems. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80°C (176°F) is recommended. Drying time is dependent on moisture level.
- Applications
From flexible packaging for food and consumer products to vacuum bagging for industrial goods, Aegis® packaging grade resins are widely used in a variety of applications, including:
- Processed meats and cheeses
- Coffee, nuts and spices
- Snacks and frozen foods
- Pet foods
- Detergent bags
- Composite fabrications
- Medical devices
- Novelty balloons
Properties
- Physical Form
- Typical Properties
Value Units Test Method / Conditions Density 1.13 g/cm3 ASTM D-792 Extractable Content max. 0.8 % SOP-702-307 Melt Flow Rate (at 235°C/1.0 kg (455°F/1.0 kg)) 1.2 g/10min ASTM D-1238 Melting Point 220 (428) °C (°F) ASTM D-3418 Moisture (24 Hour) 1.6 % ASTM D-570 Moisture (50% RH) 2.7 % ASTM D-570 Moisture (Saturation) 9.5 % ASTM D-570 Moisture Content max. 0.08 % ASTM D-6869 RV (at 96% Sulfuric Acid) 3.75 - - Viscosity (FAV) 135 - ASTM D-789 - Film Properties
Value Units Test Method / Conditions Carbon Dioxide Permeability 72.8 (4.6) cc.25μm/m²/day (cc.mil/100 in²/day) - Elmendorf Tear Strength - MD (at 23°C (73°F)) 860 N ASTM D-1922 Elmendorf Tear Strength - TD (at 23°C (73°F)) 990 N ASTM D-1922 Elongation - MD (at 23°C (73°F)) 330 % ASTM D-882 Elongation - TD (at 23°C (73°F)) 330 % ASTM D-882 Graves Tear - MD (at 23°C (73°F)) 2170 N ASTM D-1004 Graves Tear - TD (at 23°C (73°F)) 2380 N ASTM D-1004 Nitrogen Permeability 14.0 (0.9) cc.25μm/m²/day (cc.mil/100 in²/day) - Oxygen Permeability (at 23°C (73°F)/0% RH) 40.3 (2.6) cc.25μm/m²/day (cc.mil/100 in²/day) D-3958 Puncture Index - MD (at 23°C (73°F)) 470 gm/mil ASTM D-5478 Puncture Strength - MD (at 23°C (73°F)) 1050 grams ASTM D-5478 Tensile Modulus - MD (at 23°C (73°F)) 660 MPa ASTM D-882 Tensile Modulus - TD (at 23°C (73°F)) 640 MPa ASTM D-882 Tensile Strength - MD (at 23°C (73°F)) 90 MPa ASTM D-882 Tensile Strength - TD (at 23°C (73°F)) 90 MPa ASTM D-882 Tensile Yield - MD (at 23°C (73°F)) 30 MPa ASTM D-882 Tensile Yield - TD (at 23°C (73°F)) 30 MPa ASTM D-882 Water Vapor Permeability (at 38°C (100°F)/100% RH) 992 (64) gm.25μm/m²/day (gm.mil/100 in²/day) F-1249 - Molded Properties
Value Units Test Method / Conditions Flexural Modulus - MD (at 23°C (73°F)) 2610 MPa ASTM D-790 Flexural Strength - MD (at 23°C (73°F)) 100 MPa ASTM D-790 Heat Deflection Temperature - MD (at 23°C (73°F)) 55 (131) °C (°F) ASTM D-648 Notched Izod - MD (at 23°C (73°F)) 60 J/m ASTM D-256 Tensile Modulus - MD (at 23°C (73°F)) 2630 MPa ASTM D-882 Tensile Strength - MD (at 23°C (73°F)) 80 MPa ASTM D-882 Yield Elongation - MD (at 23°C (73°F)) 4.1 % ASTM D-882
Regulatory & Compliance
- Certifications & Compliance
- Regulatory Compliance
AdvanSix has more than 50 years of experience in the development and production of packaging resin that is safe and reliable for consumers and businesses. Aegis® packaging resins are manufactured to meet the stringent standards required of materials involved in the processing, handling and packaging of food. They meet all applicable U.S. Food and Drug Administration (FDA) and European Union (EU) food grade regulations, as outlined in FDA 21 CFR 177.1500 and Regulation (EU) No. 10/2011.
Technical Details & Test Data
- Extrusion Guidelines
Melt Viscosity vs. Temperature
Melt Temperature: 220°C (428°F)
Melt Temperature Range: 232°C (450°F) to 271°C (520°F).
Two key factors affect the melt viscosity (stiffness or fluidity of the melt):- The molecular weight (Mw) of the resin: Higher Mw resins will have a higher melt viscosity than lower Mw resins.
- Temperature of the melt for any given Mw resin: Higher process temperatures will provide a more fluid melt viscosity than lower process temperatures.
Typical Barrel Profile for Cast Films
Barrel: 230-260°C (446-500°F)
Adapter: 260-266°C (500-510°F)
Die: 260°C (500°F)
Process Melt Temperature: 260-270°C (500-518°F)Typical Barrel Profile for Tubular (Blown) Films
Barrel: 246-254°C (474-490°F)
Adapter: 260°C (500°F)
Die: 254°C (490°F)
Process Melt Temperature: 254-260°C (490-500°F)Screw Parameters
Metering Section: 40%
Transition Section: 3 to 4 flights
Feed Section: Balance of screw length
Compression Ratio: 3.5:1 to 4.0:1
L/D Ratio: 24:1Metering Section Flight Depth
Screw Diameter Recommended Depth 1" 0.055" 1.5" 0.060" 2" 0.070" 2.5" 0.080" 3.5" 0.100" 4.5" 0.115" 6" 0.135"