Aegis® PIR-H100MP resin from AdvanSix contains 100% post-industrial recycled (PIR) raw materials while providing the same top performance and processability as Aegis® H100MP, its standard, non-recycled counterpart.Aegis® PIR-H100MP resin is a lubricated, nucleated, medium-viscosity nylon 6 extrusion grade homopolymer for cast or blown film applications. It features a combination of strength, toughness, and thermoforming properties along with excellent heat, chemical and abrasion resistance.

Polymer Name: Polyamide 6 (PA 6)

Additives Included: Lubricant (Unspecified), Nucleating Agent

Labeling Claims: Contains PIR Resin, Food Contact Acceptable, Recycled, Sustainable

Processing Methods: Blown Film Extrusion, Cast Film Extrusion, Extrusion, Film Extrusion, Thermoforming

Density:: 1,130.0 kg/m³

Technical Data Sheet

Ask AdvanSix Questions

Thomas Clark avatarEd Asirvatham avatarJohn Facinelli avatar
View All Documents

Enhanced TDS

Identification & Functionality

Additives Included
Lubricant (Unspecified),
Nucleating Agent
Chemical Family
Polyamides
Polymer Name
Polyamide 6 (PA 6)
Plastics & Elastomers Functions
Resin
Technologies
Plastics
Product Families
Plastics — Basic Thermoplastics
Recycled Polymers
Plastics — Engineering & Specialty Polymers
Polyamides

Features & Benefits

Labeling Claims
Contains PIR Resin,
Food Contact Acceptable,
Recycled,
Sustainable
Materials Features
Abrasion Resistant,
Chemical Resistant,
Fast Crystallization,
Food Contact Acceptable,
Good Strength,
Heat Resistance,
Homopolymer,
Improved Toughness,
Lubricated,
Medium Viscosity,
Nucleated

Applications & Uses

Markets
Consumer Goods,
Food & Nutrition,
Healthcare & Pharma,
Printing & Packaging
Applications
Consumer Goods — Other Consumer Goods Applications
Printing & Packaging — Packaging
Food & Beverage Packaging,
Industrial & Transport Packaging
Plastics & Elastomers End Uses
Balloons,
Biaxially Oriented Film,
Book Covers,
Cast Films,
Film,
Flexible Packaging,
Form Fill Seal Packaging,
Oriented Film,
Pouches Flexible Packaging,
Profiles,
Retort Pouches,
Tubing
Plastics & Elastomers Processing Methods
Blown Film Extrusion,
Cast Film Extrusion,
Extrusion,
Film Extrusion,
Thermoforming
Application

Aegis® PIR-H100MP is a lubricated and nucleated medium viscosity nylon 6 extrusion grade homopolymer for cast or blown film applications

Properties

Physical Form
Pellets,
Solid
Thermal Properties
ValueUnitsTest Method / Conditions
Melting Point220 (428)°C (°F)ASTM D-3418
Typical Properties
ValueUnitsTest Method / Conditions
Density1.13g/cm³ASTM D-792
Extractable Contentmax. 0.8%SOP-702-307
Melt Flow Rate (at 235°C/1.0 kg or 455°F/1.0 kg)2.6g/10 minASTM D-1238
RV (at 96% Sulfuric Acid)3.35--
Viscosity (FAV)100-ASTM D-789
Molded Properties
ValueUnitsTest Method / Conditions
Flexural Modulus - MD* (at 73°F (22.7°C)2650MPaASTM D-790
Flexural Modulus - MD* (at 73°F (22.7°C)110MPaASTM D-790
Heat Deflection Temperature - MD* (at 73°F ( 23°C))61 (142)ºC (ºF)ASTM D-648
Notched Izod - MD* (at 73°F (23°C))60J/mASTM D-256
Tensile Modulus - MD* (at 73°F (23°C))3240MPaASTM D-882
Tensile Strength - MD* (at 73°F (23°C))80MPaASTM D-882
Yield Elongation - MD* (at 73°F (23°C), 0% RH)3.8%ASTM D-882
Mechanical Properties (Film)
ValueUnitsTest Method / Conditions
Elmendorf Tear Strength - MD* (at 23°C (73°F))880NASTM D-1922
Elmendorf Tear Strength - TD* (at 23°C (73°F))950NASTM D-1004
Elongation - MD* (at 23°C (73°F))340%ASTM D-882
Elongation - TD* (at 23°C (73°F))340%ASTM D-882
Graves Tear - MD* (at 73°F (23°C))2140NASTM D-1004
Graves Tear - TD* (at 73°F (23°C))2070NASTM D-882
Puncture Index - MD*(at 73°F (23°C))470gm/milASTM D-5478
Puncture Strength - MD* (at 73°F (23°C))960gramsASTM D-5478
Tensile Modulus - MD* (at 73°F (23°C))700MPaASTM D-882
Tensile Modulus - TD* (at 73°F (23°C))590MPaASTM D-5478
Tensile Strength - MD* (at 73°F (23°C))90MPaASTM D-882
Tensile Strength - TD* (at 73°F (23°C))80MPaASTM D-882
Tensile Yield - MD* (at 73°F (22.7°C), 50% RH)30MPaASTM D-882
Tensile Yield (at 73°F (22.7°C), 50% RH)30MPaASTM D-882
Gas Barrier Properties
ValueUnitsTest Method / Conditions
Carbon Dioxide Permeability (at 23°C (73°F), 0% RH)72.8cc/m²/day-
Nitrogen Permeability (at 73°F (23°C), 0% RH)14cc/m²/day-
Oxygen Permeability (at 73°F (23°C), 0% RH)40.3cc/m²/dayD-3958
Water Vapor Permeability (at 100°F (38°C), 100% RH )992gm-mil/m²/dayF-1249
Moisture Properties
ValueUnitsTest Method / Conditions
Moisture (24 Hour)1.6%ASTM D-570
Moisture (50% RH)2.7%ASTM D-570
Moisture (Saturation)9.5%ASTM D-570
Moisture Contentmax. 0.08%ASTM D-6869
Note

Aegis® PIR-H100MP conforms to FDA requirements of 21 CFR 177.1500 as well as EU Directive 2011/10/EC. Aegis® PIR-H100MP homopolymer possesses the combination of strength, toughness and thermoforming properties associated with nylon 6 as well as excellent heat, chemical and abrasion resistance.

Note

*Note: MD = Machine Direction and TD = Traverse Direction. Test samples obtained from 2-mil thick unoriented cast film.

Note for Mechanical Properties

Processing conditions for test specimens: melt temperature = 240ºC (464ºF); mold temperature = 80ºC (176ºF).

Regulatory & Compliance

Certifications & Compliance
EC Regulation 2011/10,
FDA 21 CFR 177.1500,
FDA 21 CFR Regulations,
FDA Compliant

Technical Details & Test Data

Extrusion Guidelines

Melt Viscosity vs. Temperature

Melt Temperature: 220°C (428°F)
Melt Temperature Range: 232°C (450°F) to 271°C (520°F).
Two key factors affect the melt viscosity (stiffness or fluidity of the melt) :
1. The molecular weight (Mw) of the resin: Higher Mw resins will have a higher melt viscosity than lower Mw resins.
2. Temperature of the melt for any given Mw resin: Higher process temperatures will provide a more fluid melt viscosity
than lower process temperatures.

 

Typical Barrel Profile for Cast Films

Barrel: 230-260°C (446-500°F)
Adapter: 260-266°C (500-510°F)
Die: 260°C (500°F)
Process Melt Temperature: 260-270°C (500-518°F)

 

Typical Barrel Profile for Tubular (Blown) Films

Barrel: 246-254°C (474-490°F)
Adapter: 260°C (500°F)
Die: 254°C (490°F)
Process Melt Temperature: 254-260°C (490-500°F)

 

Screw Parameters

Metering Section: 40%
Transition Section: 3 to 4 flights
Feed Section: Balance of screw length
Compression Ratio: 3.5:1 to 4.0:1
L/D Ratio: 24:1

 

Metering Section Flight Depth

Screw Diameter Recommended Depth
1" 0.055"
1.5" 0.060"
2" 0.070"
2.5" 0.080"
3.5" 0.100"
4.5" 0.115"
6" 0.135"

 

Storage & Handling

Processing Guidelines

Material Handling

Aegis® PIR-H100MP is supplied in sealed containers and drying prior to processing is not required. However, higher moisture is the primary cause of processing issues. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80°C (176°F) is recommended. Drying time is dependent on moisture level. More information about safe handling procedures can be obtained by requesting the Safety Data Sheet.