Aegis® H100ZP is a medium viscosity, nylon 6 extrusion grade homopolymer for cast or blown film applications. The resin product complies with all food contact regulations. Aegis® H100ZP homopolymer combines strength, toughness and thermoforming properties with excellent heat, chemical and abrasion resistance.

Polymer Name: Polyamide 6 (PA 6)

Processing Methods: Blown Film Extrusion, Cast Film Extrusion, Extrusion, Film Extrusion, Thermoforming

Technical Data Sheet

Ask AdvanSix Questions

Thomas Clark avatarEd Asirvatham avatarJohn Facinelli avatar
View All Documents

Enhanced TDS

Identification & Functionality

Chemical Family
Polyamides
Polymer Name
Polyamide 6 (PA 6)
Plastics & Elastomers Functions
Resin
Technologies
Plastics
Product Families
Plastics — Engineering & Specialty Polymers
Polyamides

Features & Benefits

Labeling Claims
Food Contact Acceptable
Materials Features
Abrasion Resistant,
Chemical Resistant,
Food Contact Acceptable,
Good Strength,
Heat Resistance,
Homopolymer,
Improved Toughness,
Medium Viscosity,
Neat Resin

Applications & Uses

Markets
Automotive & Transportation,
Consumer Goods,
Electrical & Electronics,
Industrial,
Printing & Packaging
Applications
Automotive & Transportation — Automotive
Aftermarket Parts & Components,
Interior,
Powertrain & UTH,
Safety Systems,
Tires
Industrial — Chemical & Industrial Manufacturing
Equipment & Parts
Electrical & Electronics — Devices & Assemblies
Automotive Electronics
Industrial — Leather & Textiles
Technical Fabrics,
Textile Manufacturing
Consumer Goods — Other Consumer Goods Applications
Printing & Packaging — Packaging
Food & Beverage Packaging,
Industrial & Transport Packaging
Consumer Goods — Sports & Recreation
Plastics & Elastomers End Uses
Airbags,
Automotive Applications,
Balloons,
Book Covers,
Cooling Hoses,
Fans,
Flexible Packaging,
Form Fill Seal Packaging,
Gears,
High Strength Fiber,
Industrial Applications,
Industrial Fiber Applications,
Industrial Film Applications,
Levers,
Monofilaments,
Netting,
Paper Machine Clothing,
Pouches Flexible Packaging,
Profiles,
Radiator,
Retort Pouches,
Seat Belts,
Seat Webbing,
Shrouds,
Textile Applications,
Tire Cord,
Tubing
Plastics & Elastomers Processing Methods
Blown Film Extrusion,
Cast Film Extrusion,
Extrusion,
Film Extrusion,
Thermoforming
Processing Guidelines

Material Handling

Aegis® H100ZP is supplied in sealed containers and drying prior to processing is not required. However, high moisture is the primary cause of processing problems. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80°C (176°F) is recommended. Drying time is dependent on moisture level.

Properties

Physical Form
Pellets
Typical Properties
ValueUnitsTest Method / Conditions
96% SAV3.37--
Carbon Dioxide Permeability (at 23°C (73°F)/0% RH)72.8 (4.697)cc/m2 /day (cc/100 in2 /day)-
Density1.13g/cm3ASTM D-1505
Equilibrium Moisture (at 50% RH)2.7%-
Extractable Contentmax. 0.8%-
Melt Flow Rate (at 235°C/1.0 kg (455°F/1.0 kg))2.6g/10 minASTM D-1238
Melting Point220 (428)°C (°F)ASTM D-3418
Moisture Contentmax. 0.08%-
Nitrogen Permeability (at 23°C (73°F)/0% RH)14.0 (0.903)cc/m2 /day (cc/100 in2 /day)-
Oxygen Permeability (at 23°C (73°F)/0% RH)40.3 (2.600)cc/m2 /day (cc/100 in2 /day)-
Saturation Moisture Content9.5%-
Viscosity (FAV)100-ASTM D-789
Water Absorption (in 24 hrs)1.6%-

Regulatory & Compliance

Certifications & Compliance
EC Regulation 2011/10,
FDA 21 CFR 177.1500,
FDA 21 CFR Regulations,
FDA Compliant

Technical Details & Test Data

Extrusion Guidelines

Melt Viscosity vs. Temperature

Melt Temperature: 220°C (428°F)
Melt Temperature Range: 232°C (450°F) to 271°C (520°F)
Two key factors affect the melt viscosity (stiffness or fluidity of the melt):

  • The molecular weight (Mw) of the resin: Higher Mw resins will have a higher melt viscosity than lower Mw resins.
  • Temperature of the melt for any given Mw resin: Higher process temperatures will provide a more fluid melt viscosity than lower process temperatures.

Typical Barrel Profile for Cast Films

Barrel: 230-260°C (446-500°F)
Adapter: 260-266°C (500-510°F)
Die: 260°C (500°F)
Process Melt Temperature: 260-270°C (500-518°F)

Typical Barrel Profile for Tubular (Blown) Films

Barrel: 246-254°C (474-490°F)
Adapter: 260°C (500°F)
Die: 254°C (490°F)
Process Melt Temperature: 254-260°C (490-500°F)

Screw Parameters

Metering Section: 40%
Transition Section: 3 to 4 flights
Feed Section: Balance of screw length
Compression Ratio: 3.5:1 to 4.0:1
L/D Ratio: 24:1

Metering Section Flight Depth

Screw Diameter Recommended Depth
1" 0.055"
1.5" 0.060"
2" 0.070"
2.5" 0.080"
3.5" 0.100"
4.5" 0.115"
6" 0.135"